Single Liquid Type: TAB Series High Alcohol Resistant and Wear Resistant Single Component Coating
The TA series has good adhesion and excellent workability.
- Product Description
-
Product Features
The TA series has good adhesion and excellent workability.
Applicable Products
Suitable for home appliances, toys, 3C electronic products, etc.
Applicable Substrates
ABS, PS, HIPS, PC, and other substrates
Construction Instructions (Construction Process Guidelines)
Workpiece inspection --> Workpiece surface cleaning --> Original oil stirring (Stir for three minutes to ensure the paint is evenly dispersed.) --> Dilute the original oil (viscosity reaches 9-11 seconds) --> Confirm furnace temperature (furnace temperature: 60±5℃) --> Workpiece spraying --> Workpiece inspection --> Qualified product packaging.
Construction Conditions
Product Name TAB series high alcohol and wear-resistant single-component coating Diluent W-TA series diluent Dilution Ratio Oil: Diluent = 1:1.5-2.5 (depending on customer application and workpiece)WorkProcess and workpiece dependent) Construction Viscosity 9-11 seconds (NK#2/25±1℃) Spray Gun Nozzle Diameter 1.0-1.5mm Spray Gun Air Pressure 3-5Kg/cm² Product Name TAB series high alcohol and wear-resistant single-component coating Spraying Distance 15-20cm Dry Film Thickness 8-13μm Construction Environment Temperature: 5-40℃ / Humidity: 40-80% Surface Drying Conditions Room temperature × 5~10 minutes Baking Conditions 65±5℃ × 30 minutes Performance (The following data represents the performance of UV coatings for mobile phones)
Test Items Test Methods Test Results Adhesion Cross-cut method, 3M600 tape peel test 5B Hardness Mitsubishi UNI Japanese paint pencil, weight 500gf, 45-degree angle ≥HB Alcohol Resistance 99.7% ethanol, weight 500gf, frequency: 40 times (back and forth) / minute ≥200 times no visible bottom Moisture and Heat Resistance 40℃ × 90% RH × 120H No significant change in the paint film surface Cold and Heat Cycle (-20℃ × 2H - Room temperature × 1H - 60℃ × 2H - Room temperature × 1H) 10 cycles No significant change in the paint film surface Precautions
1. Please stir thoroughly before use;
2. Please refer to the 'Construction Process Guidelines' for oil removal, degreasing, and dust removal on the workpiece before use;
3. Please use the appropriate filter mesh for filtration;
4. If performance testing is to be conducted, please bake under conditions of 65±5℃ × 2H, then cool for 30 minutes before testing;
5. Due to the different types of rubber parts and molding conditions, please confirm fully before using our coatings to ensure compatibility;
6. When humidity is too high, in addition to adding necessary anti-whitening solvents, it is recommended to enter the drying tunnel or oven immediately after coating to prevent whitening;
7. The coating film should not be too thin or too thick; if too thin, it will not provide protection, and if too thick, it may affect the chemical resistance test during recoating.
Product Consulting
20 years of R & D and production of coatings
Contact Us
Mr.Bi:
Address: Zhe Ming Kichuang Park, 89 Ma Jun Street, Nansha District, Guangzhou City, Guangdong Province
E-mail:zhemingnewmateri@qq.com
Social Media
WeChat Public Number