UV curing: piano black + dual-cure UV varnish
Good adhesion, excellent leveling, high fullness, and superior chemical resistance.
- Product Description
-
Applicable Products
Car interior central control, air conditioning vents, etc.
Applicable Substrates
ABS+PC, PC and other substrates
Construction Instructions (Construction Process Guidelines)
Workpiece inspection → Workpiece surface cleaning → Original oil stirring (stir for three minutes to disperse the paint evenly
) → Original oil thinning (viscosity reaches 9-11 seconds) → Confirm furnace temperature (furnace temperature: 60±5℃) → Workpiece spraying → Workpiece inspection → Qualified product packaging
Construction Conditions
Product Name
UV Curing: Piano Black + Dual-Curing UV Coating
Product Name
UV Curing: Piano Black + Dual-Curing UV Coating
Oil and Water Opening
QW-TA Series
Spraying Distance
15-20cm
Oil Ratio
Oil: Solid: Water = 10:1:3
Dry Film Thickness
28-33μm
Construction Viscosity
9'5-10'5 seconds (NK#2/25±1℃)
Construction Environment
Temperature: 5-40℃ / Humidity: 40-80%
Spray Gun Nozzle Diameter
1.0-1.5mm
Surface Drying Conditions
Room Temperature × 5-10 minutes
Spray Gun Air Pressure
3-5Kg/cm²
Curing Energy
700-900mj/cm²
Performance
Test Items
Test Methods
Test Results
Adhesion
Cross-cut method, 3M600 tape peel test
5B
Hardness
Mitsubishi UNI Japanese paint pencil, weight 500gf, 45-degree angle
F
Moisture and Heat Resistance
85℃×90%RH×240H
No significant change on the paint film surface
Cold and Hot Cycle
(-20℃×2H - Room Temperature×1H - 60℃×2H - Room Temperature×1H) 10 cycles
No significant change on the paint film surface
Boiling Water Resistance
100℃/2H
Next:
Product Consulting
20 years of R & D and production of coatings