Single liquid type: WJP series PVC toy paint
The WJP series has good adhesion and excellent workability.
- Product Description
-
Applicable Products
Suitable for PVC toy surface coating
Applicable Substrates
PVC and other substrates
Construction Instructions (Construction Process Guidelines)
Workpiece inspection → Workpiece surface cleaning → Original oil stirring (stir for three minutes to ensure paint is evenly dispersed
) → Original oil thinning (viscosity reaches 9-11 seconds) → Process spraying (air dry at room temperature for more than 24H) → Workpiece inspection → Qualified product packaging
Construction Conditions
Product Name
WJP Series PVC Toy Coating
Product Name
WJP Series PVC Toy Coating
Thinner
W-TP Series Thinner
Spraying Distance
15-20cm
Thinner Ratio
Oil: Thinner = 1:1.5 (depending on customer construction process and workpiece)
Dry Film Thickness
8-13μm
Construction Viscosity
9-11 seconds (NK#2/25±1℃)
Construction Environment
Temperature: 5-40℃ / Humidity: 40-80%
Spray Gun Nozzle Diameter
1.0-1.5mm
Surface Drying Conditions
Room temperature × 5-10 minutes
Spray Gun Air Pressure
3-5Kg/cm²
Baking Conditions
Air dry at room temperature for 24 hours
Performance (The following data represents the performance of UV coatings for mobile phones)
Test Items
Test Methods
Test Results
Adhesion
Cross-cut method, 3M600 tape peel test
5B
Hardness
Mitsubishi UNI Japanese paint pencil, weight 500gf, 45-degree angle
/
Alcohol Resistance
99.5% ethanol, weight 500gf, frequency: 40 times (back and forth) / minute
≥50 times no visible substrate
Moisture and Heat Resistance
40℃×90%RH×120H
No significant change on the paint film surface
Cold and Hot Cycle
(-20℃×2H - Room temperature×1H - 60℃×2H - Room temperature×1H) 10 cycles
No significant change on the paint film surface
Precautions
1. Please stir well before use;
2. Please refer to the 'Construction Process Guidelines' for oil removal, degreasing, and dust removal on the workpiece before use;
3. Please use the appropriate filter mesh for filtration;
4. Due to the different types of rubber parts and molding conditions, please confirm fully before using our coatings to ensure their adaptability;
5. When humidity is too high, in addition to adding necessary anti-whitening solvents, it is recommended to enter the drying tunnel or oven immediately after coating to prevent whitening;
6. The coating film should not be too thin or too thick; if too thin, it will not provide protection, and if too thick, it may affect the chemical resistance test during re-coating.
Product Consulting
20 years of R & D and production of coatings
Contact Us
Mr.Bi:
Address: Zhe Ming Kichuang Park, 89 Ma Jun Street, Nansha District, Guangzhou City, Guangdong Province
E-mail:zhemingnewmateri@qq.com
Social Media
WeChat Public Number