Baking paint: TK series hardware baking paint
The TK series hardware baking paint features high gloss, high leveling, resistance to boiling water, acid and alkali resistance, high wear resistance, suitable for electrostatic spraying, and suitable for wet-on-wet spraying.
- Product Description
-
Applicable Products
Applied to household appliances, cabinets, lighting and other products
Applicable Substrates
Stainless steel, aluminum alloy, zinc alloy, electroplating, galvanized sheet, etc.
Construction Instructions (Construction Process Guidelines)
Workpiece inspection → Workpiece surface cleaning → Original oil stirring (stir for three minutes to evenly disperse the paint
) → Original oil thinning (viscosity reaches 9-13 seconds) → Confirm furnace temperature UV energy (furnace temperature 150±5℃) → Workpiece spraying → Workpiece inspection → Qualified product packaging
Construction Conditions
Product Name
TK Series Hardware Baking Paint
Product Name
TK Series Hardware Baking Paint
Thinner
W-TP Series Thinner
Spraying Distance
15-20cm
Thinner Ratio
Oil: Thinner = 1:1.5-1
Dry Film Thickness
20±2μm
Construction Viscosity
9-13 seconds (NK#2/25±1℃)
Construction Environment
Temperature: 5-40℃ / Humidity: 40-80%
Spray Gun Nozzle Diameter
1.0-1.5mm
Surface Drying Conditions
Room temperature × 5-10 minutes
Spray Gun Air Pressure
3-5Kg/cm²
Baking Conditions
150℃ × 30 minutes
Performance (The following data represents the performance of UV coatings for mobile phones)
Test Items
Test Methods
Test Results
Adhesion
Cross-cut method, 3M600 tape peel test
5B
Hardness
Mitsubishi UNI Japanese paint pencil, weight 500gf, 45-degree angle
≥2H
Alcohol Resistance
99.5% ethanol, weight 500gf, frequency: 40 times (back and forth) / min
≥100 times no visible bottom
Butanone Resistance
Analytical grade butanone, weight 500gf, frequency: 40 times (back and forth) / min
≥50 times no visible bottom, no obvious discoloration
Acid Resistance Test
Soak gauze in 50% acetic acid:50% lactic acid = 1:1, press against the paint film surface, place at room temperature for 1 hour, rinse with water and observe the paint film surface
No abnormalities
Salt Spray Test
Neutral salt spray, continuous spraying for 168 hours, corrosion ≤1mm
No abnormalities
Boiling Water Resistance Test
Half of the test panel placed in boiling water, continuously heated with an induction cooker, boiled for 2 hours, after removing the test panel, let it sit for 30 minutes and observe the surface and measure adhesion
Appearance without abnormalities, adhesion: 5B
Moisture and Heat Resistance
60℃ × 95%RH × 240H
No significant changes on the paint film surface
Cold and Hot Cycle
(-20℃ × 2H - Room temperature × 1H - 60℃ × 2H - Room temperature × 1H) 10 cycles
No significant changes on the paint film surface
Precautions
1. Please stir well before use;
2. Please perform pretreatment as needed, such as ultrasonic cleaning, phosphating, sandblasting, etc.;
3. Please use the appropriate filter for filtration;
4. The coating should not be too thin, as too thin will not provide protection, and too thick may cause bubbling.
Product Consulting
20 years of R & D and production of coatings
Contact Us
Mr.Bi:
Address: Zhe Ming Kichuang Park, 89 Ma Jun Street, Nansha District, Guangzhou City, Guangdong Province
E-mail:zhemingnewmateri@qq.com
Social Media
WeChat Public Number